Polyvinyl Alcohol is manufactured by polymerization of vinyl acetate monomer, followed by hydrolysis of the polyvinyl acetate. HOP...

More information

Polyvinyl Alcohol Introduction

Polyvinyl Alcohol is a water soluble and biodegradable synthetic polymer. It is adry solid, and is available in granule and powder...

More information
polyvinyl alcohol bags hopeway
The advantages of HW PVA as a mold release agent are listed as following.

●Good film forming property, without cracking

●Anti-adhesive release effect, even when thinly applied

●Impermeability of PVA film to the organic material used, e.g. styrene

●The PVA film which adhesives to the cast article can be peeled off by hand 

Add 25 ml of N/10 NaOH solution, seal the flask and leave it still for at least 2 hours in room temperature.Add

accurately 25 ml of N/10 H2SO4 solution and titrate back the excess amount of H2SO4 solution present with

N/10 NaOH solution using phenolphthalein as the indicator, until the solution appears in pale pink color.

The volume of N/10 NaOH solution consumed in this titration is a ml. Carry out a blank test separately; the

volume of N/10 NaOH solution consumed in this blank test is b ml.

A : wt % of residual acetate groups

B : mole % of residual acetate groups

C : mole % of hydrolysis of the sample

S : weight of the initial sample

P : Purity =100 - volatile of the sample - NaAc content of the sample

F : concentration factor of N/10 NaOH solution